Table 4: Predicted mechanical properties of the as received and heat-treated samples.
| Sample name | Phase | Microhardness | Macroharness | Mechanical Properties | ||
| Bainite % | HV | HRC | HRC | YS (MPa) | TS (MPa) | |
| HTS.6 | 95 | 375.32 | 38.45 | 34.29 | 988.52 | 1301.64 |
| HTS.3 | 63 | 287.19 | 26.97 | 30.6 | 735.07 | 972.58 |
| HTS.5 | 55 | 291.82 | 27.69 | 29.42 | 748.36 | 989.84 |
| HTS.4 | 46 | 270.77 | 24.48 | 29.64 | 687.83 | 911.25 |
| HTS.2 | 45 | 262.03 | 24.03 | 31.08 | 662.71 | 878.64 |
| HTS.1 | 35 | 224.12 | 17.52 | 25.50 | 553.67 | 737.07 |
| Pearlite % | HV | HRC | HRC | YS (MPa) | TS (MPa) | |
| As received | 75 | 249.7 | 22.22 | 25.50 | 627.22 | 832.56 |