In this paper, Nd: YAG laser welding of TC4 Ti alloy and SUS301L stainless steel (SS) dissimilar metal material was carried using Ni interlayer by laser offset. The laser was focused on the SS side of the joint, which joined the SS and Ni interlayer by fusion welding. At SS-Ni interface, a weld zone was formed due to dilution of the Ni and mixing with the SS. At the Ti alloy-Ni interface, a metallurgical reaction was responsible for joining. The presence of unmelted Ni interlayer ensured that crack free welds were obtained and no brittle Ti-Fe intermetallics were observed. Tensile strength of the joint can reach to 178 MPa.
TC4 Ti alloy, 304 stainless steel, Welding, Microstructure, Filler metal
Ti alloy has been broadly applied in various industrial fields as characterized by high strength, good toughness, low density, high temperature resistance and good corrosion resistance [1]. Yet its application has been restrained by the high cost of Ti alloy, poor weldability and processing performance, poor creep resistance. Stainless steel (abbreviated as SS) was the most commonly used structural material, with numerous excellent properties, such as weldability, wear resistance, mechanical properties, and relatively low cost [2]. Recently, the dissimilar joint of Ti alloy and SS has been highly demanded in aerospace and nuclear industries [3]. However, owing to the poor metallurgical compatibility and significant mismatch in physical and mechanical properties, the joining of Ti alloy to SS is facing to a great difficulty [4-6]. Direct fusion welding of Ti alloy and SS can form various intermetallics, such as TiFe and TiFe2, etc. These highly brittle Ti-Fe intermetallics make conventional fusion-welded joints cracked spontaneously. Therefore, the weld was very brittle and easy to crack under residual stress.
The general method to address this problem is to use interlayer between Ti alloy and SS to prevent the formation of brittle Ti-Fe intermetallics. The interlayers such as Cu, Ag, Ni, Al and Mg have been employed to restrain the formation of Ti-Fe intermetallics during welding [7-9]. The tensile strength of pulsed laser welding dissimilar joint of TC4 Ti alloy to 301L SS using Cu as an interlayer reached 340 MPa, as found by XiaoYan Gu, et al. [10]. Using Cu as interlayer can greatly reduce the brittleness of the weld. As their studies suggest, the amount of brittle Ti-Fe intermetallics decreased in the joint. Yet brittle Cu-Ti intermetallics, such as CuTi2 were formed. Accordingly, it is concluded that Ti-Fe intermetallics are inevitably formed in the welding if the interlayer is fully melted. Accordingly, the Ti and Fe elements will react in the weld pool, producing Ti-Fe intermetallics in the welding as long as the interlayer is completely melted. Researchers are trying to minimize the mixing of matrix materials to prevent the formation of these brittle phases, indeed even low mixing cannot avoid the formation of brittle Ti-Fe intermetallics. By one pass welding, XiaoYan Gu, et al. [11] studied pulsed laser welding of SUS 301L SS to TC4 Ti alloy via pure Nb interlayer. The joint was formed with one welding zone and a reaction layer separated by residual unmelted Nb interlayer. The unmelted Nb interlayer served as a diffusion barrier between Ti and Fe to restrain the formation of Ti-Fe intermetallics. The mechanical performance of the joint was determined by the reaction layer at the Nb-SS interface with a tensile strength of 370 MPa. Yet Fe-Nb intermetallics were formed in the reaction layer, which decreased the mechanical property of the joints. How to ensure the quality of the joint is mainly to suppress or avoid the formation of Ti-Fe intermetallic compounds, we should solve these problems. However, the appropriate process parameters and the location of the laser beam spot must be selected to control the formation of the reaction layer in joint. Therefore, this process is too cumbersome and not suitable for industrial production.
Moreover, solid-state welding can eliminate the problems in the direct fusion welding because the base metals remain in the solid state during joining and many successful examples have been reported [12-14]. As the noted results suggest, these two dissimilar materials can be joined by using diffusion bonding [12], friction [13] and explosive welding [14]. They have concluded that at low loads formation of intermetallics could be totally avoided. However, the service conditions may make particular processes unsuitable. The diffusion process needs a long time to implement in general. Taking high temperature applications for example, brazing cannot be candidate. Furthermore, the required joint geometry can make friction welding and explosive welding difficult to apply.
Based on the foregoing analysis, it is likely to prevent the formation of Ti-Fe intermetallics in the welding if the interlayer is not completely melted. In the meantime, laser welding, as an efficient and flexible non-contact welding technology, has made major achievements in the connection of refractory materials and dissimilar materials. Accordingly, laser served as the welding heat source of Ti alloy and SS. As mentioned earlier, the prepare process of diffusion welding is complicated, and the welding process takes a long time and is inefficient. Therefore, using the advantages of laser welding energy density concentration, controllability, high efficiency and speed, two welding mechanisms (fusion welding and diffusion welding) are combined to avoid melting and liquid mixing of the base metals during welding, and the advantages of the two welding methods are complementary.
The base materials used in this experiment were TC4 alloy and 304 SS. Their chemical compositions and physical properties are given in Table 1, Table 2 and Table 3. It can be seen that there are large differences in thermal conductivity and linear expansion coefficient between the two base materials, which would lead to large temperature gradient and thermal stress in the joint during welding process. The specimens for direct welding experiments were machined into 100 mm × 80 mm × 1 mm plates. The filler metal used was 0.5 mm Ni plate. Before welding, the specimens were mechanically and chemically cleaned. The gap between the edges of the Ti alloy and SS was very important to adequate heat transfer and prevent porosity formation. The specimens are clamped each other tightly in order to get the minimum gap formation between the edges. CW laser was used with average power of 1.20 kW, wavelength of 1080 nm and beam spot diameter of 0.1 mm. A schematic diagram of the welding procedure is shown in Figure 1. In order to ensure that Ni was not completely melted, the laser beam was focused on the SS plate 0.5 mm away from the SS interface. The welding parameters were: laser beam power of 456 W, defocusing distance of +5 mm, welding speed of 650 mm/min. Argon gas with the purity of 99.99% was applied as a shielding gas with total flow of 20 L/min at top of the joint.
Specimens for microstructural characterization were prepared metallographically and then etched using a reagent containing 2 ml HNO3 and 6 ml HF. The microstructure of joints were studied by optical microscopy (Scope Axio ZEISS), scanning electron microscope SEM (S-3400) with fast energy dispersion spectrum EDS analyzer and selected area XRD (X'Pert3 Powder) analysis. The operating voltage of XRD was 15 kV and the current was 20 mA using a Cu target. Scanning span was 20°-90° (2θ) with a speed of 3° per minute. The tensile strength of the joints was evaluated at room temperature in tensile testing machine (MTS Insight 10 kN) at a cross head speed of 0.2 mm/min.
The Optical Microscope (OM) image of the cross section of the joint is shown in the Figure 2a. It was found that three regions were formed at the joint, namely, the weld zone of Ni-SS interface, the unmelted Ni and the reaction layer of Ti alloy-Ni interface. The formation of Ti-Fe intermetallics was not found in the weld zone, which was attributed to the presence of unmelted Ni. Because the microstructure of the weld zone at Ni-SS interface is quite different from that of the reaction layer at Ti alloy-Ni interface, the reaction layer becomes black after corrosion. Figure2b presents the optical microscopy image before corrosion of the Ti alloy-Ni interface. It does not present such defects as pores and macro-cracks. In addition, unmelted Ni was beneficial to release and adjust the thermal stress of Ti alloy-SS joint, thus improving the mechanical properties of the joint. The physical model of the joint formation is shown in Figure 3. The laser beam was focused on the side of the SS plate, resulting into producing a molten pool with small holes inside the SS and Ni plate and absorbing a lot of heat (Figure 3a). Thus, the edge of the Ni as the keyhole boundary melted sharply due to the high absorption of the laser inside the keyhole. The unmelted part of Ni interlayer absorbing a significant amount of heat from the welding pool and transferring it to the Ti alloy side [15]. Hence, the interdiffusion of Ti and Ni atoms at Ti alloy-Ni interface could be promoted due to the high temperature of unmelted Ni (Figure 3b). In Figure 3c, metallurgical reaction occurred at Ti alloy-Ni interface to produce reaction layer. Because of the high thermal conductivity of SS, solidification of weld pool and liquid in the joint started from SS side, which could form a mixed joint between welding zone and reaction layer, as shown in Figure 3c and Figure 3d.
It should be noted that precise control of the laser spot position is crucial to obtain a sound joint. If the laser spot is far away from the Ni-SS interface, metallurgical reaction of Ti and Ni at the Ti alloy-Ni interface cannot take place. If the laser spot is draw near to the Ni-SS interface, the Ni interlayer is beginning to melt in the joint, thereby amount of brittle Ti-Fe intermetallics is greatly increased in the joint and cannot be realized the effective combination between dissimilar materials of Ti alloy and SS.
The OM image of the weld zone is shown in Figure 4a and no defects were observed in it. The cellular dendritic structure was well evident in weld zone. The main chemical composition of weld zone (see Table 4) was nearly 57.2 wt.% Fe and 27.2 wt.% Ni. In accordance with the Ni-Fe binary phase diagram, the primary microstructure of weld zone was (γFe, Ni) solid solution. In the weld zone, the columnar grain that grows in the center of the weld is located near the fusion line of the two sides, and there are small cell crystal areas in the welding center (Figure 4b). The OM image of reaction layer at Ti alloy-Ni interface is shown in Figure 4c. It was indicated that the reaction layer was a layered structure. The SEM image of the reaction layer is shown in Figure 4d. According to EDS analysis results in Table 4, main composition in reaction layer was of 56.1 wt.% of Ti and 44.0 wt.% of Ni. Based on the EDS analyses results and Ti-Ni binary phase diagram, the main microstructure of reaction layer was defined as TiNi+TiNi3 phase. The width of the reaction layer was 3.4 μm. According to metal physics knowledge, the greater the thickness of the reaction zone, the greater the cumulative brittleness of the reaction zone [16]. In addition, the high cooling rate inhibited the growth of dendritic structures in the reaction layer. Therefore, a fine dendritic structure was obtained in the reaction layer, which contributed to the minimum brittleness of the reaction layer, thereby improving the mechanical properties of the joint.
The maximum tensile strength of the joint was about 178 MPa (Figure 5a). The joint fractured reaction layer at Ti alloy-Ni interface during tensile tests (Figure 5b). Figure 5c shows fracture surface of the joint exhibiting typical brittle characteristics. Moreover, as shown in Figure 5d, XRD analyses of fracture surface detected TiNi and TiNi3 phases. This confirmed the presence of Ti-Ni intermetallics at fracture surfaces. It should be noted that there was no Ti-Fe intermetallics in the weld zone and reaction layer. The reaction layer at Ti alloy-Ni interface became the weak zone of the joint, which led to the failure in the tensile test.
Dissimilar laser welding of Ti alloy to SS was achieved using a Ni interlayer. Unmelted Ni interlayer acted as a barrier to mixing of the two base materials, which prevented the formation of brittle Ti-Fe intermetallics, while ensuring joining at both interfaces. At the Ni-SS interface, a weld zone formed by fusion welding. No intermetallics except for (γFe, Ni) solid solution were produced in the weld zone and cellular dendritic structure was observed. At the Ti alloy-Ni interface, a reaction layer formed by metallurgical reaction. The reaction layer mainly contained TiNi and TiNi3. The tensile strength can reach to 178 MPa.