Summery of mechanical properties of Ni-42.5 wt.% Ti-7.5 wt.% Cu at different time and temperature aging.

Table 1: Summery of mechanical properties of Ni-42.5 wt.% Ti-7.5 wt.% Cu at different time and temperature aging.

	As-rolled	Aging	10 min	1 h	8 h	16 h
	As-rolled	Time Aging Temp.	10 min	1 h	8 h	16 h
Fracture stress (MPa)	272.3	400 ℃	300.14	559.74	611.05	545.38
Fracture strain (%)	0.95	400 ℃	1.02	1.04	1.33	1.22
Fracture stress (MPa)	272.3	700 ℃	339.25	421.31	409.78	406.33
Fracture strain (%)	0.95	700 ℃	0.95	1.9	3.63	4.01